Description
API 5ct Q125 Casing:
Q125 Casing is placed downhole to provide structural integrity to the wellbore and must withstand external-collapse pressure from rock formations and internal-yield pressure from fluid and gas. It must also hold its own deadweight and withstand the torque and transaxial pressure placed on it while running downhole.
API 5ct Q125 casing tubing specification
Q125 api casing or tubing is a relatively common one in oil drilling. Because of the low steel grade of Q125, it is used for shallow Oil and Gas extraction. Due to its low Price among other grades of steel, it enjoys broader applications. Q125 API casing or tubing is widely used in the extraction of natural gas and coalbed methane, and can be commonly found in shallow wells, geothermal wells, and water wells.
API 5CT Q125 Casing Tubing Type of Casing：
API 5CT Q125 Casing Tubing Chemical composition:
| Chemical Composition, mass Fraction (%) | ||||||||||||||
| Grade | C | Mn | Mo | Cr | Ni | Cu | P | S | Si | |||||
| Type | min | max | min | max | min | max | min | max | max | max | max | max | max | |
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 | 13 | 14 | 15 |
| H40 | — | — | — | — | — | — | — | — | — | — | — | — | 0.03 | — |
| J55 | — | — | — | — | — | — | — | — | — | — | — | — | 0.03 | — |
| k55 | — | — | — | — | — | — | — | — | — | — | — | — | 0.03 | — |
| n80 | 1 | — | — | — | — | — | — | — | — | — | — | 0.03 | 0.03 | — |
| N80 | Q | — | — | — | — | — | — | — | — | — | — | 0.03 | 0.03 | — |
| R95 | — | — | 0.45 c | — | 1.9 | — | — | — | — | — | — | 0.03 | 0.03 | 0.45 |
| l80 | 1 | — | 0.43 a | — | 1.9 | — | — | — | — | 0.25 | 0.35 | 0.03 | 0.03 | 0.45 |
| L80 | 9Cr | — | 0.15 | 0.3 | 0.6 | 0.9 | 1.1 | 8 | 10 | 0.5 | 0.25 | 0.02 | 0.03 | 1 |
| L80 | 13Cr | 0.15 | 0.22 | 0.25 | 1 | — | — | 12 | 14 | 0.5 | 0.25 | 0.02 | 0.03 | 1 |
| C90 | 1 | — | 0.35 | — | 1.2 | 0.25 b | 0.85 | — | 1.5 | 0.99 | — | 0.02 | 0.03 | — |
| T95 | 1 | — | 0.35 | — | 1.2 | 0.25 b | 0.85 | 0.4 | 1.5 | 0.99 | — | 0.02 | 0.03 | — |
| C110 | — | — | 0.35 | — | 1.2 | 0.25 | 1 | 0.4 | 1.5 | 0.99 | — | 0.02 | 0.03 | — |
| p110 | e | — | — | — | — | — | — | — | — | — | — | 0.030 e | 0.030 e | — |
| Q125 | 1 | — | 0.35 | 1.35 | — | 0.85 | — | 1.5 | 0.99 | — | 0.02 | 0.01 | — | |
| NOTE elements shown shall be reported in product analysis. | ||||||||||||||
| a The carbon content for L80 may be increased up to 0.50 % maximum if the product is oil-quenched or polymer-quenched. | ||||||||||||||
| b The molybdenum content for Grade C90 Type 1 has no minimum tolerance if the Wall thickness is less than 17.78 mm. | ||||||||||||||
| c The carbon content for R95 may be increased up to 0.55 % maximum if the product is oil-quenched. | ||||||||||||||
| d The molybdenum content for T95 Type 1 may be decreased to 0.15 % minimum if the wall thickness is less than 17.78 mm. | ||||||||||||||
| e For EW Grade P110, the phosphorus content shall be 0.020 % maximum and the sulfur content 0.010 % maximum. | ||||||||||||||