Well Used in Oil Field API5CT L80 N80 Casing Tubing
Benefits of Using API5ct l80 n80 Casing tubing in oil field operations API5CT L80 n80 casing tubing is a popular choice in the oil field industry due to its durability and reliability. This type of casing tubing is well-suited for a variety of applications, making it a versatile option for oil field operations. One of…
Benefits of Using API5ct l80 n80 Casing tubing in oil field operations
API5CT L80 n80 casing tubing is a popular choice in the oil field industry due to its durability and reliability. This type of casing tubing is well-suited for a variety of applications, making it a versatile option for oil field operations. One of the key benefits of using API5CT L80 N80 casing tubing is its High strength and resistance to corrosion. This makes it ideal for use in harsh environments where other types of casing tubing may not hold up as well. The high strength of API5CT L80 N80 casing tubing also allows for deeper drilling depths, making it a valuable asset in oil field operations.
In addition to its strength and durability, API5CT L80 N80 casing tubing is also known for its excellent performance in high-pressure and high-temperature environments. This makes it a reliable choice for oil field operations where these conditions are common. The ability of API5CT L80 N80 casing tubing to withstand extreme conditions makes it a valuable asset for oil field operators looking to maximize efficiency and productivity.
| Chemical composition, mass Fraction (%) | ||||||||||||||
| grade | C | Mn | Mo | Cr | Ni | Cu | P | S | Si | |||||
| Type | min | max | min | max | min | max | min | max | max | max | max | max | max | |
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 | 13 | 14 | 15 |
| H40 | — | — | — | — | — | — | — | — | — | — | — | — | 0.03 | — |
| J55 | — | — | — | — | — | — | — | — | — | — | — | — | 0.03 | — |
| k55 | — | — | — | — | — | — | — | — | — | — | — | — | 0.03 | — |
| N80 | 1 | — | — | — | — | — | — | — | — | — | — | 0.03 | 0.03 | — |
| N80 | Q | — | — | — | — | — | — | — | — | — | — | 0.03 | 0.03 | — |
| R95 | — | — | 0.45 c | — | 1.9 | — | — | — | — | — | — | 0.03 | 0.03 | 0.45 |
| L80 | 1 | — | 0.43 a | — | 1.9 | — | — | — | — | 0.25 | 0.35 | 0.03 | 0.03 | 0.45 |
| L80 | 9Cr | — | 0.15 | 0.3 | 0.6 | 0.9 | 1.1 | 8 | 10 | 0.5 | 0.25 | 0.02 | 0.03 | 1 |
| L80 | 13Cr | 0.15 | 0.22 | 0.25 | 1 | — | — | 12 | 14 | 0.5 | 0.25 | 0.02 | 0.03 | 1 |
| c90 | 1 | — | 0.35 | — | 1.2 | 0.25 b | 0.85 | — | 1.5 | 0.99 | — | 0.02 | 0.03 | — |
| T95 | 1 | — | 0.35 | — | 1.2 | 0.25 b | 0.85 | 0.4 | 1.5 | 0.99 | — | 0.02 | 0.03 | — |
| C110 | — | — | 0.35 | — | 1.2 | 0.25 | 1 | 0.4 | 1.5 | 0.99 | — | 0.02 | 0.03 | — |
| p110 | e | — | — | — | — | — | — | — | — | — | — | 0.030 e | 0.030 e | — |
| Q125 | 1 | — | 0.35 | 1.35 | — | 0.85 | — | 1.5 | 0.99 | — | 0.02 | 0.01 | — | |
| NOTE elements shown shall be reported in product analysis. | ||||||||||||||
| a The carbon content for L80 may be increased up to 0.50 % maximum if the product is oil-quenched or polymer-quenched. | ||||||||||||||
| b The molybdenum content for Grade C90 Type 1 has no minimum tolerance if the Wall thickness is less than 17.78 mm. | ||||||||||||||
| c The carbon content for R95 may be increased up to 0.55 % maximum if the product is oil-quenched. | ||||||||||||||
| d The molybdenum content for T95 Type 1 may be decreased to 0.15 % minimum if the wall thickness is less than 17.78 mm. | ||||||||||||||
| e For EW Grade P110, the phosphorus content shall be 0.020 % maximum and the sulfur content 0.010 % maximum. | ||||||||||||||